Bimetallic PdAg nanoparticle arrays from monolayer films of diblock copolymer micelles
2015
MICROSCOPIE+ATARI+EEH:GMA:TBG:NSP:MAO; International audience; The self-assembly technique provides a highly efficient route to generate well-ordered structures on a nanometer scale. In this paper, well-ordered arrays of PdAg alloy nanoparticles on flat substrates with narrow distributions of particle size (6-7 nm) and interparticle spacing (about 60 nm) were synthesized by the block copolymer micelle approach. A home-made PS-b-P4VP diblock copolymer was prepared to obtain a micellar structure in toluene. Pd and Ag salts were then successfully loaded in the micellar core of the PS-b-P4VP copolymer. A self-assembled monolayer of the loaded micelles was obtained by dipping the flat substrate …
X-ray Spectroscopy of (Ba,Sr,La)(Fe,Zn,Y)O3-δIdentifies Structural and Electronic Features Favoring Proton Uptake
2020
Mixed protonic–electronic conducting oxides are key functional materials for protonic ceramic fuel cells. Here, (Ba,Sr,La)(Fe,Zn,Y)O3−δ perovskites are comprehensively investigated by X-ray spectroscopy (in oxidized and reduced states). Extended X-ray absorption fine structure shows that Zn,Y doping strongly increases the tendency for Fe–O–Fe buckling. X-ray absorption near-edge spectroscopy at the Fe K-edge and X-ray Raman scattering at the O K edge demonstrate that both iron and oxygen states are involved when the samples are oxidized, and for the Zn,Y doped materials, the hole transfer from iron to oxygen is less pronounced. This can be correlated with the observation that these material…